Olefins, block copolymers higher, polymerization

The dual function of the precatalysts 4 opened the way to well-controlled block polymerization of ethylene and MMA (eq. (5)) [89, 90]. Homopolymerization of ethylene (Mn = 10000) and subsequent copolymerization with MAA (Mn 20000) yielded the desired linear AB block copolymers. Mono and bis(alkyl/silyl)-substituted flyover metallocene hydride complexes of type 8 gave the first well-controlled block copoymerization of higher a-olefins with polar monomers such as MMA or CL [91]. In contast to the rapid formation of polyethylene [92], the polymerization of 1-pentene and 1-hexene proceeded rather slowly. For example, AB block copolymers featuring poly( 1-pentene) blocks (M 14000, PDI = 1.41) and polar PMMA blocks (M 34000, PDI = 1.77) were obtained. Due to the bis-initiating action of samarocene(II) complexes (Scheme 4), type 13-15 precatalysts are capable of producing ABA block copolymers of type poly(MMA-co-ethylene-co-MMA), poly(CL-co-ethylene-co-CL), and poly(DTC-co-ethylene-co-DTC DTC = 2,2-dimethyltrimethylene carbonate) [90]. 

As described in Section 9.1.2.2.3, several lanthanocene alkyls are known to be ethylene polymerization catalysts.221,226-229 Both (188) and (190) have been reported to catalyze the block copolymerization of ethylene with MMA (as well as with other polar monomers including MA, EA and lactones).229 The reaction is only successful if the olefin is polymerized first reversing the order of monomer addition, i.e., polymerizing MMA first, then adding ethylene only affords PMMA homopolymer. In order to keep the PE block soluble the Mn of the prepolymer is restricted to <12,000. Several other lanthanide complexes have also been reported to catalyze the preparation of PE-b-PMMA,474 76 as well as the copolymer of MMA with higher olefins such as 1-hexene.477... 

---