Natural rubber dynamic mechanical test

Dynamic mechanical measurements for elastomers that cover wide ranges of frequency and temperature are rather scarce. Payne and Scott [12] carried out extensive measurements of /a and /x" for unvulcanized natural mbber as a function of test frequency (Figure 1.8). He showed that the experimental relations at different temperatures could be superposed to yield master curves, as shown in Figure 1.9, using the WLF frequency-temperature equivalence, Equation 1.11. The same shift factors, log Ox. were used for both experimental quantities, /x and /x". Successful superposition in both cases confirms that the dependence of the viscoelastic properties of rubber on frequency and temperature arises from changes in the rate of Brownian motion of molecular segments with temperature. 

Table 2.5 summarises the main applications of thermal analysis and combined techniques for polymeric materials. Of these, thermomechanical analysis (TMA) and dynamic mechanical analysis (DMA) provide only physical properties of a very specific nature and yield very little chemical information. DMA was used to study the interaction of fillers with rubber host systems [40]. Thermomechanical analysis (TMA) measures the dimensional changes of a sample as a function of temperature. Relevant applications are reported for on-line TMA-MS cfr. Chp. 2.1.5) uTMA offers opportunities cfr. Chp. 2.1.6.1). The primary TA techniques for certifying product quality are DSC and TG (Table 2.6). Specific tests for which these techniques are used in quality testing vary depending upon the type of material and industry. Applications of modulated temperature programme are (i) study of kinetics (ii) AC calorimetry (Hi) separation of sample responses (in conjunction with deconvolution algorithms) and (iv) microthermal analysis.

---