Morphology in the melting range

Ueda et al. [26] recently investigated a flow-oriented PE-fr-aPP diblock copolymer with Mw = 113 000 (Mn/Mw = 1.1) and a PE volume fraction of 0.48. This diblock copolymer is in the strong segregation regime (i.e., estimated xN = 10.5 and Todt = 290 °C) and has a lamellar morphology in the melt. They found a breakout phenomenon with the formation of spherulites in an intermediate crystallization temperature range 95 < Tc < 101 °C. At crystallization temperatures above 101 °C or below 95 °C spherulites were not formed and the crystallization was confined within the lamellar MD. Ueda et al. report that lamellar MD and spherulites do not co-exist when the material crystallizes from the melt which is separated in lamellar MDs. In other words, in this particular case, breakout or confined crystallization within lamellar MDs depends on the crystallization conditions. 

The melting range, obtained directly from thermal analysis, obviously contains information on polymer morphology and, in particular, on the crystallite size distribution within the specimen, but to date this correlation is no more than a qualitative description. There are, however, obvious differences in the melting ranges of polyethylenes of different molecular weight averages and distributions, and with different thermal histories. "... 

---