Localized corrosion dealloying

Mechanisms of SCC. Crack initiation of EAC is complex and not well understood till now. Most of the SCC systems exhibit short initiation times ranging from minutes to weeks and cracking often occurs due to the change in the environment rather than to a very long initiation time. Stress-corrosion crack growth rates are usually 10 11 and 10-6 m s In systems such as stainless steels in chloride solutions, localized corrosion may create the local conditions prone to crack development, but it is still difficult to explain the initiation of the crack in the absence of localized corrosion in environmental conditions different from that of the crack propagation.95 It should be mentioned that dealloyed surface layers such as certain copper alloys in ammonia-containing solutions are believed to cause SCC.54... 

C A state of surface dealloying with no continuous oxide, e.g., gold alloys in many aqueous solutions [75,99]. Dealloying may also occm within localized corrosion sites in passive alloys such as austenitic stainless steels. 

Corrosion reactions can occur by a simple dissolution mechanism, whereby the containment material dissolves in the melt without any impurity effects. Material dissolved in a hot zone may be redeposited in a colder area, possibly compounding the corrosion problem by additional plugging and blockages where deposition has taken place. Dissolution damage may be of a localized nature, for example, by selective dealloying. The second corrosion mechanism is one of reactions involving interstitial (or impurity) elements such as carbon or oxygen in the melt or containment material. Two further subforms are corrosion product formation and elemental transfer. In the former the liquid metal is directly involved in corrosion product formation. In the latter the liquid metal does not react directly with the containment alloy rather, interstitial elements are transferred to, from, or across the liquid. 

---