Influence of Crack Growth Resistance Curve Upon Failure by Fracture

Influence of Crack Growth Resistance Curve Upon Failure by Fracture [Pg.621]

Furthermore, by considering differing initial defect sizes, Oq, it can be seen that the effective fracture toughness at failure will increase with the length of the initial defect, although the failure stress will decrease. [Pg.621]