Coupling agents studies

Table 2.2 Structural parameters for GOTHS and THVS selected structural parameters calculated using the different DFT functionals and the DFTB method for the two silane coupling agents studied in this work.

Table 7.2 summarizes recent works reported on silica admicellar polymerization of polyisoprene. The silica modified by admicellar polymerization was reported by researchers as having superior performance compared to those reinforced with unmodified silica or silica modified with typical silane coupling agents. Studies also showed that the use of surfactant can influence performance of the rubber composite. ... 

As mentioned earlier, the contact-mechanics-based experimental studies of interfacial adhesion primarily include (1) direct measurements of surface and interfacial energies of polymers and self-assembled monolayers (2) quantitative studies on the role of interfacial coupling agents in the adhesion of elastomers (3) adhesion of microparticles on surfaces and (4) adhesion of viscoelastic polymer particles. In these studies, a variety of experimental tools have been employed by different researchers. Each one of these tools offers certain advantages over the others. These experimental studies are reviewed in Section 4. 

Studies on adhesion of elastomers role of interfacial chains and coupling agents... 

The toughness of interfaces between immiscible amorphous polymers without any coupling agent has been the subject of a number of recent studies [15-18]. The width of a polymer/polymer interface is known to be controlled by the Flory-Huggins interaction parameter x between the two polymers. The value of x between a random copolymer and a homopolymer can be adjusted by changing the copolymer composition, so the main experimental protocol has been to measure the interface toughness between a copolymer and a homopolymer as a function of copolymer composition. In addition, the interface width has been measured by neutron reflection. Four different experimental systems have been used, all containing styrene. Schnell et al. studied PS joined to random copolymers of styrene with bromostyrene and styrene with paramethyl styrene [17,18]. Benkoski et al. joined polystyrene to a random copolymer of styrene with vinyl pyridine (PS/PS-r-PVP) [16], whilst Brown joined PMMA to a random copolymer of styrene with methacrylate (PMMA/PS-r-PMMA) [15]. The results of the latter study are shown in Fig. 9. 

The adhesion promotion of an organic matrix to an inorganic substrate using a silane has been studied to model the structure of the created interphase [64-66]. The polymer/silane interphase is influenced by the solubility parameter of both the silane coupling agent and the polymer. More interdiffusion occurs when the solubility parameters of the polymer and the silane closely match together. It is believed that this model can be applied to silicone adhesive/solid substrate system. 

Jones, F.R., Interfacial aspects of glass fibre reinforced plastics. In Jones, F.R. (Ed.), Interfacial Phenomena in Composite Materials. Butterworths, London, 1989, pp. 25-32. Chaudhury, M.K., Gentle, T.M. and Plueddemann, E., Adhesion mechanism of poly(vinyl chloride) to silane primed metal surfaces. J. Adhes. Sci. Technol, 1(1), 29-38 (1987). Gellman, A.J., Naasz, B.M., Schmidt, R.G., Chaudhury, M.K, and Gentle, T.M., Secondary neutral mass spectrometry studies of germanium-silane coupling agent-polymer interphases. J. Adhes. Sci. Technol., 4(7), 597-601 (1990). 

Ethylene-vinyl acetate Fetterman [37] reinforced compounded ethylene-vinyl acetate (EVA) copolymer by using short hbers and found that silane coupling agents were effective at establishing improved hber-matrix adhesion. Das et al. [38] prepared carbon fiber-filled conductive composites based on EVA and studied the electromagnetic interference shielding effectiveness of the composites. 

Fibres reacted with pre-heated MAPP always exhibited larger contact angles compared with fibres reacted with as-received MAPP. FTIR studies showed that there was a higher level of ester linkages when the fibres were reacted with the pre-heated MAPP. Wood polymer composites were made by shear mixing in a twin screw extmder, and the mechanical properties of these composites were found to be superior when pre-heated MAPP was used as the coupling agent. 

---