Conducting doping increases conductivity greatly

Polymers. The Tt-conjugated polymers used in semiconducting appHcations are usually insulating, with semiconducting or metallic properties induced by doping (see Flectrically conductive polymers). Most of the polymers of this type can be prepared by standard methods. The increasing use of polymers in devices in the last decade has led to a great deal of study to improve the processabiUty of thin films of commonly used polymers. 

As future outlook, it would be of great relevance to be able to eventually enhanee the intrinsic conductivity of CNTs. In this respect, the latest development in alkali metal intercalated CNTs looks rather promising. In faet, Chauvet et al. recently sueeeeded to dope aligned CNT by potassium and found that the Pauli susceptibility increases a factor of 3 upon doping, indicating that K-doped tubes are still good eonductors [23]. 

Enzymatically synthesized polyphenol derivatives are expected to have great potential for electronic applications. The surface resistivity of poly(p-phe-nylphenol) doped with nitrosylhexafluorophosphate was around 105 Q.4a The iodine-labeled poly(catechol) showed low electrical conductivity in the range from 10 6 to 10 9 S/cm.48 The iodine-doped thin film of poly (phenol- co- tetradecyloxyphenol) showed a conductivity of 10 2 S/cm, which was much larger than that obtained in aqueous 1,4-dioxane.24a The third-order optical nonlinearity (%3) of this film was 10 9 esu. An order of magnitude increase in the third-order nonlinear optical properties was observed in comparison with that prepared in the aqueous organic solution. 

---