Several minerals and trace elements are vital to the human organism and must be ingested with daily food in sufficient amounts. Wine can contribute not only minerals containing potassium, calcium, and magnesium but also numerous essential trace elements, such as chromium, cobalt, iron, fluorine, copper, selenium, and zinc, among others. The contents found in wine are very low ranging from mg L 1 to igL, sometimes even lower. 

When iron and selenium are heated together to a high temperature, combination takes place, but the product usually contains more selenium than corresponds to the monoselenide or ferrous selenide, FeSe. By heating the product m hydrogen, however, the monoselenide results,7 8 further reduction to a sub-selenide not taking place, although the selenides of nickel and cobalt are reduced to sub-selenides under like conditions. 

INCO produced electrolytic nickel at its refinery in Port Colborne, Ontario, Canada. The production started in 1926. The anodes were made by reducing nickel oxide with coke, and the anodes contained about 93.5% Ni, 4% Cu, and 1% Co. The sulfur content was low, about 0.6%. The approximate composition of the purified electrolyte was 60 g L-1 Ni2+, 95 g L-1 S042-, 35 g L-1 Na+, 55 g L-1 Cl , and 16 g L 1 boric acid, and the temperature was 60 °C. The current density of the process was 16 A/sq.ft (approximately 170 A m-2) and the cell voltage was about 1.6 V. At the normal cell operating voltage, the principal impurities - iron, cobalt, lead, arsenic, and copper - dissolved into the solution with nickel. Silver, gold, the PGMs, sulfur, selenium, and tellurium fell to the bottom of the cell as an insoluble slime. The produced cathodes... 

The INCO, Thompson plant in Manitoba, Canada, electrolyzes 240 kg sulfide anodes in a sulfate-chloride electrolyte. The approximate composition of the electrolyte is 60 g L x Ni2+, 95 g L 1 SC>42, 35 g L 1 Na+, 60 g L 1 Cl-, and 16 g L 1 H3BO4, and the temperature is 60 °C. Nickel, cobalt, and copper dissolve from the anode, while sulfur, selenium, and the noble metals form an insoluble sludge or slime, from which they can be recovered. The anode sludge contains 95% elemental sulfur, sulfide sulfur, nickel, copper, iron, selenium, and precious metals. Nickel is deposited on to pure nickel starting sheets. The anode cycle is 15 days and the cathode cycle is 5 to 10 days. Electrolysis is carried out at a current density of 240 A m-2 giving a cell voltage of 3 to 6 V [44, 46]. 

Neutron activation analysis has also been employed sporadically for the determination of trace elements in protein fractions, collagen, nucleic acids as well as in biochemicals containing activatable elements (e.g., cobalt in vitamin B12 or selenium in selenoaminoacids). 

---