Catalyst nickel/ceria/zirconia

Hoekman et al. [40] studied CO2 methanation reaction over Haldor Topspe commercially available methanation catalysts consisting of Ni and NiO on an alumina substrate with total nickel loading of 20-25% and an operating temperature range of 190-450 C in an extruded ring-shaped catalyst. Approximately 60% conversion of CO2 was observed at r= 300-350°C and stoichiometric CO2/H2 ratio. Aldana et al. [41] found that Ni over ceria-zirconia (prepared by sol-gel synthesis) shows an initial COj activity of almost 80%, with a CH4 selectivity of 97.3%, decreasing down to 84.7% after 90 hours of reaction. By IR operando analysis, they found that for Ni-ceria-zirconia catalysts the main mechanism for CO2 methanation does not require CO as reaction intermediate and the mechanism is based on CO2 adsorption on weak basic sites of the support. 

A marked effect of the Ce02/Zr02 composition (in samples containing 40 wt.% NiO) on the catalytic activity was noticed. The catalysts with Ce Zr =1 1 (6A) were not only more active (than 7A and 8A) but were also stable during the reaction. Sample 8A containing no zirconia in the support showed a low activity. The NiO crystallite size (Table 11.2) in these compositions varied in the order 7A < 6A < 8A. It may be recalled that on ceria-based catalysts the crystallite size of nickel metal was similar to that of NiO. The higher activity for 6A than 7A indicates that in addition to accessibility of... 

The anodes consisting of a nickel catalyst and of cermet mixed with yttria-doped zirconia electrolyte that are used in conventional solid oxide fuel cells also lose their ability to work at lower temperatures because of a loss of conductivity by the ceramic. This suggests that, for the ceramic in the anode, a material having a higher conductivity at intermediate temperatures should be used. It was in fact shown that an anode made with a nickel/samaria-doped ceria cermet has a much lower polarization than the conventional variant. 

---