Actinide carbides metallothermic reduction

The yield and rate of the tantalothermic reduction of plutonium carbide at 1975 K are given in Fig. 3. Producing actinide metals by metallothermic reduction of their carbides has some interesting advantages. The process is applicable in principle to all of the actinide metals, without exception, and at an acceptable purity level, even if quite impure starting material (waste) is used. High decontamination factors result from the selectivities achieved at the different steps of the process. Volatile oxides and metals are eliminated hy vaporization during the carboreduction. Lanthanides, Y, Ti, Zr, Hf, V, Nb, Ta, Mo, and W form stable carbides, whereas Rh, Os, Ir, Pt, and Pd remain as nonvolatile metals in the actinide carbides. Thus, these latter elements... 

This process is particularly useful for the preparation of pure plutonium metal from impure oxide starting material (111). It should also be applicable to the preparation of Cm metal. Common impurities such as Fe, Ni, Co, and Si have vapor pressures similar to those of Pu and Cm metals and are difficult to eliminate during the metallothermic reduction of the oxides and vaporization of the metals. They are eliminated, however, as volatile metals during preparation of the actinide carbides. 

Actinide metals with very low vapour pressures (U,Np,Pu) have been obtained by metallothermic reduction of their carbides by non-volatile reductants (Ta, W) (3) ... 

All of the actinide elements are metals with physical and chemical properties changing along the series from those typical of transition elements to those of the lanthanides. Several separation, purification, and preparation techniques have been developed considering the different properties of the actinide elements, their availability, and application. Powerful reducing agents are necessary to produce the metals from the actinide compounds. Actinide metals are produced by metallothermic reduction of halides, oxides, or carbides, followed by the evaporation in vacuum or the thermal dissociation of iodides to refine the metals. 

---