The glass transformation on different time scales

At first sight it would appear that the characteristics of the glass transformation observed in the simulated polymer are quantitatively quite different to what is observed on macroscopic time-scales in the laboratory. Firstly, the transition is taking place at a much higher temperature than one would 

Finally it is worth mentioning one additional reason why we might expect a different character to the glass transition as observed on very short time 

---