PMMA-based ionomer

In general, as the ion content is raised, the modulus or stiffness of the ionomer is increased, as shown by the data in Fig. 2. While the increase is much greater in the elevated temperature range, where the polymer is acting more like a crosslinked rubber, there is still a significant increase in the glassy modulus below Tg. For example, for the PMMA-based ionomer of Fig. 2, the modulus at 30°C is almost 20% above that of the homopolymer for an ionomer having an ion content of 12.4 mol%. For the... 

Studies of PMMA-based ionomers also demonstrate the influence of thermal treatment on deformation modes (16). For Na salts of PMMA-based ionomers of 6 and 12 mol% that were cast from DMF, only crazes were observed on straining. However, after an additional heat treatment (48 h at 160°C), which also removes any DMF solvent that is present, shear deformation zones are induced. Hence, the ionic cluster phase, which was destroyed by the polar solvent, has been restored by the heat treatment. 

The combined effects of a divalent Ca counterion and thermal treatment can be seen from studies of PMMA-based ionomers [16]. In thin films of Ca-salts of this ionomer cast from methylene chloride, and having an ion content of only 0.8 mol%, the only observed deformation was a series of long, localized crazes, similar to those seen in the PMMA homopolymer. When the ionomer samples were subject to an additional heat treatment (8 h at 100°C), the induced crazes were shorter in length and shear deformation zones were present. This behavior implies that the heat treatment enhanced the formation of ionic aggregates and increased the entanglement strand density. The deformation pattern attained is rather similar to that of Na salts having an ion content of about 6 mol% hence, substitution of divalent Ca for monovalent Na permits comparable deformation modes, including some shear, to be obtained at much lower ion contents. 

---