Nonbanded spherulitic morphology

HMS can crystallize in either banded or nonbanded spherulitic morphologies as illustrated in Figures 2a and 2b respectively (14). Banding is typical of HMS crystallized below 56°C whereas nonbanded spherulites are formed by crystallization above 56°C (14). Banding of polymer spherulites is thought to be related to the periodic twisting of... 

In conclusion, the deformation behavior of poly(hexamethylene sebacate), HMS, can be altered from ductile to brittle by variation of crystallization conditions without significant variation of percent crystallinity. Banded and nonbanded spherulitic morphology samples crystallized at 52°C and 60°C fail at a strain of 0.01 in./in. whereas ice-water-quenched HMS does not fail at a strain of 1.40 in./in. The change in deformation behavior is attributed primarily to an increased population of tie molecules and/or tie fibrils with decreasing crystallization temperature which is related to variation of lamellar and spherulitic dimensions. This ductile-brittle transformation is not caused by volume or enthalpy relaxation as reported for glassy amorphous polymers. Nor is a series of molecular weights, temperatures, strain rates, etc. required to observe this transition. Also, the quenched HMS is transformed from the normal creamy white opaque appearance of HMS to a translucent appearance after deformation. 

---