Nickel alloys, environment-alloy combinations resulting

Metal dusting usually occurs in high carbon activity environments combined with a low oxygen partial pressure where carburisation and graphi-tisation occur. Usually pits develop which contain a mixture of carbon, carbides, oxide and metal (Fig. 7.52). Hochmann" proposed that dusting occurs as the result of metastable carbide formation in the high carbon activity gas mixture which subsequently breaks down into metal plus free carbon. The dependence of the corrosion resistance of these nickel alloys on the protective oxide him has been described accelerated or internal oxidation occurs only under conditions that either prevent the formation, or lead to the disruption, of this him. In many petrochemical applications the pO is too low to permit chromia formation (ethylene furnaces for example) so that additions of silicon" or aluminium are commonly made to alloys to improve carburisation resistance (Fig. 7.53). 

---