Crack initiation Crevice corrosion, metallic materials

The arbitrary division of behaviour has been made because of the extreme behaviour of some chemicals that initiate small areas of attack on a well-passivated metal surface. The form of attack may manifest itself as stress-corrosion cracking, crevice attack or pitting. At certain temperatures and pressures, minute quantities of certain chemicals can result in this form of attack. Chloride ions, in particular, are responsible for many of the failures observed, and it can be present as an impurity in a large number of raw materials. This has led to the development of metals and alloys that can withstand pitting and crevice corrosion, but on the whole these are comparatively expensive. It has become important, therefore, to be able to predict the conditions where more conventional materials may be used. The effect of an increase in concentration on pitting corrosion follows a similar relationship to the Freundlich equation where... 

Schmitt [52] reviewed the effect of elemental sulfur on corrosion of construction materials (carbon steels, ferric steels, austenitic steels, ferritic-austenitic steels (duplex steels), nickel and cobalt-based alloys and titanium. Wet elemental sulfur in contact with iron is aggressive and can result in the formation of iron sulfides or in stress corrosion cracking. Iron sulfides containing elemental sulfur initiate corrosion only when the elemental sulfur is in direct contact with the sulfide-covered metal. Iron sulfides are highly electron conductive and serve to transport electrons from the metal to the elemental sulfur. The coexistence of hydrogen sulfide and elemental sulfur in aqueous systems, that is, sour gases and oils, causes crevice corrosion rates of... 

---