Crack growth subcritical mode

All the above modes of fracture are affected by the environment around the crack tip. This behaviour is typified by the phenomenon of stress-corrosion cracking where a crack, which is subjected to a subcritical stress concentration, will grow in a corrosive environment when /f, the critical stress concentration for stress-corrosion cracking). Therefore, to predict accurately the occurrence of cracking and crack growth rate, not only the materials properties are required but also information on the immediate environmental conditions. 

---