Carbon dioxide adsorption praseodymium samples

The adsorption of carbon dioxide or oxygen on praseodymium samples was measured by a constant-volume method using a calibrated Pirani vacuum gauge. Praseodymium oxide was heated in oxygen (4 kPa) at 775°C for 1 h, then evacuated at 750°C for 0.5 h just before the measurement. The sample of praseodymium oxychloride was prepared from praseodymium chloride by heating under oxygen flow... 

Adsorption of Carbon Dioxide and Oxygen on Praseodymium Samples. 

Adsorption of carbon dioxide or oxygen on the praseodymium samples was carried out in the pressure range of 1-40 Pa to evaluate the number of chemisorption sites on the samples. Praseodymium oxide irreversibly adsorbed 9.5 x 10" mol g of carbon dioxide. The amount of oxygen irreversibly adsorbed on the sample was 15.2 x 10" mol g Carbon dioxide or oxygen was not adsorbed on the samples containing chlorine, i.e., praseodymium chloride and praseodymium oxychloride prepared from the chloride by heating under oxygen flow at 750°C for 1 h. 

No adsorption of carbon dioxide or oxygen was observed on either praseodymium chloride or oxychloride. This finding is consistent with the XPS results. The main peaks at 529 eV in the spectra for praseodymium oxychloride samples are also attributed to the lattice oxygen of the oxychloride while the peaks at 531 eV are assignable to O Is for praseodymium oxide, suggesting that the surfaces of the oxychloride samples are partially oxidized to praseodymium oxide. The 3d binding energy of 933 eV for praseodymium in the chloride and oxychloride implies that the valence of praseodymium is 3+, while the shoulder at 928 eV could be attributed to metallic praseodymium (77). 

---