Ball mill HES57 mode

Fig. 2.13 Evolution of XRD patterns as a function of ball milling time of ABCR powder under the HES57 mode (high energy shearing two magnets at five and seven o clock positions) in hydrogen atmosphere under -600 kPa pressure in the magneto-mill Uni-Ball-Mill 5...

Fig. 3.6 Secondary electron micrographs showing morphology of (a) as-received NaAlH and (b) after milling for 5 h in the magneto mill Uni-BaU-MiU 5 under HES57 mode in argon (two magnets at 5 and 7 o clock positions ball to powder weight ratio 50 1)...

Fig. 3.26 Scanning electron micrographs of (MgH + 7fwt%LiAlH ) composites synthesized by ball milling in the magneto mill Uni-Ball-Mill 5 using HES57 mode for 20 h under 700 kPa argon, (a) X = 10, (b) a = 20, (c) X = 30, (d) x = 50 and (e) X = 70. All micrographs taken at the same magnification. Secondary electrons contrast...

Fig. 3.27 Dependence of the average particle size (BCD) of the composites on the content of MgH after ball milling in the magneto mill Uni-Ball-Mill 5 using HES57 mode for 20 h under 700 kPa argon...

---